Skip to main content
Q-Match & Q-Match Flow

Q-Match & Q-Match Flow

Smart shade matching universal restorative composite

  • Q-Match is a dental restorative composite intended for direct placement in all cavity classes in anterior and posterior teeth.
  • Q-Match is used for repair of enamel defects, Provisionals, porcelain restorations, minor occlusal build-ups, core build-ups, and incisal abrasions
  • Q-Match has the ability to match the complete VITA® shades spectrum with only 3 shades.
  • Q-Match is compatible with all dental adhesives available on the market.
  • Direct placement in all cavity classes in anterior and posterior teeth.
  • Repair of enamel defects, repair of Provisionals, and repair of porcelain restorations.
  • Minor occlusal build-ups, core build-ups, and incisal abrasions.
  • Q-Match is a light cured, radiopaque, resin-based restorative composite.
  • ISO 4049 classification: Type 1, Class 2, Group 1.
  • Q-Match is formulated for direct placement in any type of anterior and posterior cavity form.
  • Q-Match is intended to be used with a dental bonding agent and can be sculpted prior to curing.
  • Once light-cured, Q-Match can be easily finished and polished to achieve a highly aesthetic and durable restoration.
  • Q-Match can be dispensed via a syringe or a unit-dose capsule to provide a restoration with excellent visual color match to the surrounding dentition.
  • Q-Match is available in 3 shades: Light, Medium, Dark.
  • Q-Match has been on the market since 2023 with no changes in formula. No complaints of any health-related or chemical performance issues were received.

Technical Data (Q-Match)

  • Compressive Strength: >360 MPa
  • Flexural Strength: >160 MPa
  • Shear bond strength to enamel: >20 MPa
  • Linear/ Polymerization Shrinkage: ≤1.5%
  • Solubility: ≤7.5 μg/ mm3
  • Water Sorption: ≤40 μg/ mm3
  • Depth of cure irradiation by LED / Halogen lamp for 20 seconds: 9.0 mm
  • Radiopacity, % Aluminum: >400%
  • Light Curing Time: 10 – 20 seconds

 

Technical Data (Q-Match Flow)

  • Compressive Strength: >360 MPa
  • Flexural Strength: >170 MPa
  • Shear bond strength to enamel: >30 MPa
  • Linear/ Polymerization Shrinkage: ≤1.5%
  • Solubility: ≤7.5 μg/ mm3
  • Water Sorption: ≤40 μg/ mm3
  • Depth of cure irradiation by LED / Halogen lamp for 20 seconds: 9.0 mm
  • Radiopacity, % Aluminum: >280%
  • Light Curing Time: 10 – 20 seconds

Instructions for Use

EN

Instructions for Use (Q-Match Flow)

EN

Scientific Literature

  1. RR-BJM-Q-Match Flow Strength-Radiopacity and Gloss Retention
  2. RR-BJM-Q-Match Flow Universal Strength-Radiopacity and Gloss Retention.pdf

Infographics

  1. Advantages; Formula Main Blocks; Test Results

SDS

Q-Match Composite EN

Q-Match Flow Floable Composite EN

100016 Q-Match Light

1 Syringe 2 ml (4 g) Q-Match Light

100017 Q-Match Medium

1 Syringe 2 ml (4 g) Q-Match Medium

100018 Q-Match Dark

1 Syringe 2 ml (4 g) Q-Match Dark

100019 Q-Match Light

20 Compules 0.125 ml (0.25 g) Q-Match Light

100020 Q-Match Medium

20 Compules 0.125 ml (0.25 g) Q-Match Medium

100021 Q-Match Dark

10 Compules 0.125 ml (0.25 g) Q-Match Dark

100022 Q-Match Flow

1 Syringe 1.2 ml (2.4 g) Q-Match Flow